Solvent resistant self drying glass screen printing ink

  The high-temperature, low-temperature, acid, alkali and mold resistant ink of oules is prepared from * * imported special resin materials, imported pigments, additives, solvents and other raw materials and combined through fine grinding
It is suitable for silk screen printing and pad printing of various metal, glass, ceramics, stone, electroplating (aqueous electroplating), anodic aluminum oxide surface, electrostatic paint surface and paint baking surface, Excellent adhesion can be obtained without adding curing agent and baking
It is mainly used for industrial machinery and household appliances for specific purposes, ovens, cookers, flues, vehicle exhaust pipes, etc
which need to be resistant to high temperature, low temperature, acid, alkali and mold
Ink characteristics: high temperature resistance, low temperature resistance, acid and alkali resistance, mold resistance, smoothing, good adhesion, alcohol resistance, chemical resistance, good hand feel, good leveling, smooth surface, good surface hardness, strong impact resistance, scratch resistance, alcohol resistance, chemical resistance, scratch resistance and * *
Good high temperature resistance (long-term service temperature can reach 400 ℃ or above) and long service life; Good low temperature resistance (long-term service temperature can reach - 65 ℃ or above) and long service life; Excellent chemical corrosion resistance and mold resistance scope of application: This product is mainly used for all kinds of metal, glass, vacuum electroplating, water electroplating, electrophoresis, anodic aluminum oxide, electrolytic plate, aluminum plastic plate, plastic spraying, powder spraying, electrostatic painting surface, baking paint surface, as well as all kinds of ceiling oxidation plate, mirror panel, coated plate, roller coating plate, painting surface, UV paint surface, electroplating surface, aluminum plate Screen printing and pad printing of galvanized iron plate, stainless steel, iron, painted plate, sign, silica gel, rubber, plastic PPS, mild steel plate, white iron sheet and other products
Color: white, black, red, yellow, green, blue, purple and other colors can be customized
Usage: 1 Can be used in one component 2 Curing agent can also be added as a two-component
It is recommended to cure in a two-component way in order to achieve the - good performance state of the ink
3 It can be baked at low temperature
4
It can also be baked at high temperature
Printing methods: silk screen printing, pad printing, roll coating, coating and coverage capacity: 300 mesh screen is used, about 30-45 square meters are printed per kilogram of ink
Environmental protection level: pass the European toy safety test Sony, halogen-free test
Drying conditions: on the premise of heating and drying
The standard condition for heating and drying is to heat at 150 ℃ for 30 minutes
Please refer to the following table for drying time: (Note: with the increase of temperature and baking time, the ink film shows better adhesion and chemical resistance) temperature ℃ drying temperature ℃ 80℃   100℃   120℃   150℃   180℃   200℃   250 ℃ note: when the ambient temperature is lower than 18 ℃, do not use natural drying
Under this temperature, the ink crosslinking reaction cannot be sufficient, so it will affect the performance of the ink film