Guizhou Guiyang waterborne zinc rich primer - inorganic zinc silicate primer ordering merchants

  Keguan / guanpai Waterborne zinc rich primer Environmental friendly waterborne zinc rich primer Long term anti-corrosion primer for bridges and large steel structures; Guizhou Guiyang waterborne zinc rich primer - inorganic zinc silicate primer order: 189
8307
2660 manager Tan
Product introduction
Waterborne zinc rich primer is a two-component, waterborne quick drying epoxy zinc rich coating, which can form a good anti-corrosion coating after curing
The coating can protect local mechanical damage by providing cathodic protection
The dry film zinc content of this product reaches 80 & plusmn; 2%。
Recommended use:
As an anti-corrosion primer for waterborne steel structure coating in medium to severe atmospheric exposure environment, it is especially suitable for large steel components such as modern bridges and steel structures
It is also applicable to oil storage tank, oil transportation, inner wall of solvent warehouse, inner and outer wall of heat exchanger and underwater and underground pipelines
Film thickness and theoretical coating rate:
Low value , High value , recommend
Dry film thickness & mu; M , 50  80  sixty
Wet film thickness & mu; M , 104   167  one hundred and twenty-five
Theoretical coating rate (㎡ / L) , 9
6  6  eight
Physical properties:
Yan , Color , grey
Volume solids (%) , 48± two
Specific gravity (after mixing) , 2
3± 0
2g/ml
Flash , Point , ＞ 28℃
VOC content , 100g/L
Table Dry , About 40 minutes (20 ℃)
Fully cured , 7 days (20 ℃)
Light , , Matte
Adhesion , excellent
Water resistance , excellent
Flexibility , excellent
Surface treatment:
All surfaces to be painted shall be clean, dry and free of dirt, and the surfaces shall be evaluated and treated in accordance with international standard iso8504