Mechanical properties of TC4 Titanium Alloy TC4 mirror polished titanium plate

  TC4 / Ti-6Al-4V is what material TC4 titanium alloy chemical composition performance

1
Heat treatment of TC4 titanium alloy: MPa, solid solution strengthening treatment of TC4 material can reach 1100mpa without increasing strength, and the strength under general annealing state is 900MPa

2
Mechanical properties of TC4 titanium alloy: tensile strength & sigma; b/MPa≥ 895, predetermined residual elongation stress & sigma; r0
2/MPa≥ 825, elongation & Delta; 5（%）≥ 10
Reduce area & psi; （%）≥ twenty-five
3
Density of TC4 titanium
4
51 (g / cm3) working temperature: - 100 ~ 550 (℃)

4
Chemical composition of TC4 titanium alloy

TC4 titanium (TI) separation, iron (FE) ≤ 0
30, carbon (c) ≤ 0
10, nitrogen (n) ≤ 0
05，（H）≤ 0
015, oxygen (o) ≤ 0
20, (AL) 5
5 ~ 6
8, vanadium (V) 3
5 ~ 4
5
Characteristics of TC4

1) The composition of titanium alloy TC4 is Ti-6Al-4V, belonging to (& alpha; + & beta;) Titanium alloy, good mechanical properties
High strength
The strength sb = 1
012gpa, density g = 4
4 * 103 and specific strength sb / g = 23
5 of TC4, while the specific strength sb / g of alloy steel is less than 18

(2) The thermal conductivity of titanium alloy is low
The thermal conductivity of titanium alloy is 1 / 5 that of iron and 1 / 10 that of aluminum
The thermal conductivity of TC4 is L = 7
955 w / M? K。 The elastic modulus of titanium alloy is low
The elastic modulus of TC4 is e = 10GPa, about 1 / 2 of that of steel, so titanium alloy is prone to deformation during processing
It is mostly used in medical and aviation fields

(3) Ti-6Al-4V is a heat-treated titanium alloy with good weldability in Sheet Formability and forging properties
It is used to manufacture compressor blades and impellers of jet engines
Others, such as landing gear wheels and structural parts, fasteners, supports, aircraft accessories, frames, purlin structures, pipes, etc
, are widely used

4) The surface hardness of TC4 itself is not high, hrc30
However, the heat in the processing process will oxidize, nitride and carbonize the surface of the material, forming mixed skin such as titanium oxide, titanium dioxide, titanium oxide, titanium carbide and titanium nitride
Among them, titanium carbide is an important part of cemented carbide, and its hardness is equivalent to that of cutting tools; Titanium nitride is a kind of wear-resistant material with high hardness, which is often used for gold plating of jewelry; Titanium dioxide is an ingredient for firing ceramic glaze, and its hardness is not low (Mohs hardness is 7, 45 steel is only 5
5)
Mohs hardness is a measurement method that is not easy to plastic deformation of gemstones, ores and glass

5) Popular labels: ASTM b348 grade 2 titanium rod, manufacturer, supplier, factory, purchase, customization, quotation, free sample, titanium tube weight calculator, titanium thermal AC coil, grade 2 titanium plate, titanium shell and tube cooler, titanium alloy tube, pure titanium, DIN WS grade 2
6) TC4 titanium alloy
7) TC4 titanium alloy angle steel, TC4 titanium alloy flange, pipe fittings, steel pipe, heat exchanger and reducer, gasket, tee, pipe fittings, tubesheet, all specifications
With years of consumption experience, the chemical composition and mechanical properties of TC4 / Ti-6Al-4V titanium alloy are strictly controlled

8) Titanium alloy specification:
9) Angle steel
1mm to 1300mm
10) Steel pipe
1-1300mm, can also be customized

11) Pipe fitting size: 1 / 8 inch - 80 inch (dn6-dn2000)

12) Flange size
DN6 - DN2000
13) Length: any length requested by the customer

14) Query: TC4 / Ti-6Al-4V titanium alloy
15) TC4 / Ti-6Al-4V titanium alloy
16) TC4 / Ti-6Al-4V performance and heat treatment forgings, including TC4 / Ti-6Al-4V applications and specifications, TC4 / Ti-6Al-4V
17) Tubesheet, pipe fittings, TC4 flange, TC4 angle steel, TC4 valve, TC4 three-dimensional bending

18）
19) Appearance disposal
20) 180grid, 320grid, 400grid Satin / wool
21) 400grid, 500grid and 600grid mirror polishing
Properties and application of TC4 (GR5) titanium alloy:
Titanium alloy is now the most attractive metal material in biomedical applications
In medicine, they are used as implants to replace failed hard tissue
Examples include artificial hip joint, artificial knee joint, bone plate, screw for fracture fixation, heart valve prosthesis, pacemaker and artificial heart
Ti-6Al-4V has long been a major medical titanium alloy
However, for the application of permanent implants, the alloy may have toxic effects due to the release of vanadium and aluminum
For this reason, based on Ti-6Al-4V implants, alloys without vanadium and aluminum have been introduced into implant applications
These new alloys include Ti-6Al-7Nb (ASTM f1295), ti-13nb-13zr (ASTM f1713) and ti-12mo-6zr (ASTM f1813) & quot;